Probing nanoscale damage gradients in ion-irradiated metals using spherical nanoindentation

Siddhartha Pathak, Surya R. Kalidindi, Jordan S. Weaver, Yongqiang Wang, Russell P. Doerner, Nathan A. Mara

Research output: Contribution to journalArticlepeer-review

20 Scopus citations

Abstract

We discuss and demonstrate the application of recently developed spherical nanoindentation stress-strain protocols in characterizing the mechanical behavior of tungsten polycrystalline samples with ion-irradiated surfaces. It is demonstrated that a simple variation of the indenter size (radius) can provide valuable insights into heterogeneous characteristics of the radiation-induced-damage zone. We have also studied the effect of irradiation for the different grain orientations in the same sample.

Original languageEnglish (US)
Article number11918
JournalScientific reports
Volume7
Issue number1
DOIs
StatePublished - Dec 1 2017

Bibliographical note

Funding Information:
The authors acknowledge funding from Department of Energy, Nuclear Engineering Enabling Technologies (DOE-NEET) - Reactor Materials program # DE-FOA-0000799, and University of California Office of the President (UCOP) under Award Number 12 - LR237801 for this work. R.D. was the PI on the UCOP award. This work was performed, in part, at the Center for Integrated Nanotechnologies, an Office of Science User Facility operated for the U.S. Department of Energy (DOE) Office of Science. Los Alamos National Laboratory, an affirmative action equal opportunity employer, is operated by Los Alamos National Security, LLC, for the National Nuclear Security Administration of the U.S. Department of Energy under contract DE-AC52–06NA25396. SP gratefully acknowledges funding from the Los Alamos National Laboratory Director’s Postdoctoral Fellowship and University of Nevada, Reno start-up faculty funds for this work. The authors thank Dr. Cheng Sun (Idaho National Laboratory, ID) for help with the TEM measurements.

Publisher Copyright:
© 2017 The Author(s).

Fingerprint Dive into the research topics of 'Probing nanoscale damage gradients in ion-irradiated metals using spherical nanoindentation'. Together they form a unique fingerprint.

Cite this