Microscopical analysis of fractured restorative resin/etched enamel bonds

OMAR ZIDAN, ERIK ASMUSSEN, KNUD DREYER JORGENSEN

Research output: Contribution to journalArticle

21 Citations (Scopus)

Abstract

Abstract – The purpose of the present work was to analyze the boundary structures of fractured restorative resin/etched enamel bonds. The fracture patterns were studied by scanning electron and opdeal microscopy. The three main types of failure observed were classified as: apparent interfacial failure, failure in the bulk of the restorative resin and failure in the bulk of the enamel. The fracture of the resin/etched enamel bond in the case of the apparent interfacial failure was located in the resin very near the interface. No true interfacial debonding occurred in any of the bonds studied.

Original languageEnglish (US)
Pages (from-to)286-291
Number of pages6
JournalEuropean journal of oral sciences
Volume90
Issue number4
DOIs
StatePublished - Aug 1982

Fingerprint

Dental Enamel
Electron Scanning Microscopy

Keywords

  • dental materials
  • fracture pattern
  • operative dentistry

Cite this

Microscopical analysis of fractured restorative resin/etched enamel bonds. / ZIDAN, OMAR; ASMUSSEN, ERIK; JORGENSEN, KNUD DREYER.

In: European journal of oral sciences, Vol. 90, No. 4, 08.1982, p. 286-291.

Research output: Contribution to journalArticle

ZIDAN, OMAR ; ASMUSSEN, ERIK ; JORGENSEN, KNUD DREYER. / Microscopical analysis of fractured restorative resin/etched enamel bonds. In: European journal of oral sciences. 1982 ; Vol. 90, No. 4. pp. 286-291.
@article{d57accdf788e43a6a549a593f48d776a,
title = "Microscopical analysis of fractured restorative resin/etched enamel bonds",
abstract = "Abstract – The purpose of the present work was to analyze the boundary structures of fractured restorative resin/etched enamel bonds. The fracture patterns were studied by scanning electron and opdeal microscopy. The three main types of failure observed were classified as: apparent interfacial failure, failure in the bulk of the restorative resin and failure in the bulk of the enamel. The fracture of the resin/etched enamel bond in the case of the apparent interfacial failure was located in the resin very near the interface. No true interfacial debonding occurred in any of the bonds studied.",
keywords = "dental materials, fracture pattern, operative dentistry",
author = "OMAR ZIDAN and ERIK ASMUSSEN and JORGENSEN, {KNUD DREYER}",
year = "1982",
month = "8",
doi = "10.1111/j.1600-0722.1982.tb00739.x",
language = "English (US)",
volume = "90",
pages = "286--291",
journal = "European Journal of Oral Sciences",
issn = "0909-8836",
publisher = "Blackwell Munksgaard",
number = "4",

}

TY - JOUR

T1 - Microscopical analysis of fractured restorative resin/etched enamel bonds

AU - ZIDAN, OMAR

AU - ASMUSSEN, ERIK

AU - JORGENSEN, KNUD DREYER

PY - 1982/8

Y1 - 1982/8

N2 - Abstract – The purpose of the present work was to analyze the boundary structures of fractured restorative resin/etched enamel bonds. The fracture patterns were studied by scanning electron and opdeal microscopy. The three main types of failure observed were classified as: apparent interfacial failure, failure in the bulk of the restorative resin and failure in the bulk of the enamel. The fracture of the resin/etched enamel bond in the case of the apparent interfacial failure was located in the resin very near the interface. No true interfacial debonding occurred in any of the bonds studied.

AB - Abstract – The purpose of the present work was to analyze the boundary structures of fractured restorative resin/etched enamel bonds. The fracture patterns were studied by scanning electron and opdeal microscopy. The three main types of failure observed were classified as: apparent interfacial failure, failure in the bulk of the restorative resin and failure in the bulk of the enamel. The fracture of the resin/etched enamel bond in the case of the apparent interfacial failure was located in the resin very near the interface. No true interfacial debonding occurred in any of the bonds studied.

KW - dental materials

KW - fracture pattern

KW - operative dentistry

UR - http://www.scopus.com/inward/record.url?scp=84985756783&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84985756783&partnerID=8YFLogxK

U2 - 10.1111/j.1600-0722.1982.tb00739.x

DO - 10.1111/j.1600-0722.1982.tb00739.x

M3 - Article

C2 - 6753101

AN - SCOPUS:84985756783

VL - 90

SP - 286

EP - 291

JO - European Journal of Oral Sciences

JF - European Journal of Oral Sciences

SN - 0909-8836

IS - 4

ER -