Fabrication of zeolite films using layer-by-layer depositions

Zhiping Lai, Michael Tsapatsis, Derek Beving, Yushan Yan

Research output: Contribution to conferencePaper

Abstract

High quality zeolite films have been successfully synthesized in the last decade using hydrothermal crystallization based methods such as in situ[1] and seeded growth.[2] However, the hydrothermal process is usually very corrosive, time-consuming and costly. Here we report an alternative way to fabricate zeolite films using Layer-by-Layer depositions. In this method, thin plate-like zeolite tiles are self-assembled on substrate surface in a preferential orientation. The deposition conditions are optimized to achieve that each layer is almost a close-packed monolayer. Intercrystalline gaps are closed by overlapping between layers. Since the thickness of each zeolite tiles is very thin, so the overall thickness of the film after several depositions can be still kept in sub-micrometer range. Therefore, a thin, compact and oriented zeolite film can be achieved using this Layer-by-Layer deposition method. The zeolite we chose to demonstrate this idea is MCM-22. The precursor of zeolite MCM-22, namely MCM-22(P), is a layered aluminosilicate.[3] Layers in the as-synthesized MCM-22(P) are weakly linked together with organic structure directing agents, Hexamethyuleneimine (HMI), along the [001] direction. Two-dimensional 12MR, i.e. defined by twelve interconnected SiO4 tetrahedra, channels are running in-plane of the MCM-22(P) layers. However, the limiting apertures for transport perpendicular to the layers (along [001] direction) are 6MR's. Thus, molecules like water and O2 cannot penetrate along the c-axis. Upon calcination, MCM-22(P) condenses to MCM-22. On the other hand, layers in MCM-22(P) can be delaminated.[4] After calcination, it forms another material called ITQ-2. Either the MCM-22(P) or MCM-22 particles we synthesized have plate-like shapes with thickness of about 50 nanometers and diameter of about 1 micrometer. The thinnest dimension is along the c-axis. Delaminated layers in ITQ-2 were even thinner. These particles were deposited on substrate surfaces using methods as described in literature. [2,5,6] In these methods, the first layer of zeolite particles are covalently bonded to the substrate surface, while other physically adsorbed top layers are removed by sonication. With these methods we have successfully prepared thin, compact and highly c-oriented MCM-22 films on aluminum alloy Al-2024-T3 surfaces for corrosion protection. The film fabrication procedure, characterization results by XRD, SEM, TEM, etc., and their corrosion performance will be presented.

Original languageEnglish (US)
Number of pages1
StatePublished - Dec 1 2005
Event05AIChE: 2005 AIChE Annual Meeting and Fall Showcase - Cincinnati, OH, United States
Duration: Oct 30 2005Nov 4 2005

Other

Other05AIChE: 2005 AIChE Annual Meeting and Fall Showcase
CountryUnited States
CityCincinnati, OH
Period10/30/0511/4/05

Fingerprint Dive into the research topics of 'Fabrication of zeolite films using layer-by-layer depositions'. Together they form a unique fingerprint.

  • Cite this

    Lai, Z., Tsapatsis, M., Beving, D., & Yan, Y. (2005). Fabrication of zeolite films using layer-by-layer depositions. Paper presented at 05AIChE: 2005 AIChE Annual Meeting and Fall Showcase, Cincinnati, OH, United States.